Non-wetting refractory castable

Non-wetting aluminum castable is made by adding the com…

Composition: Al2O3=80% Refractoriness: 1750℃

Bulk Density: 2.8 g/cm3

Max working temp.: 1550℃

Compressive Strength: 95Mpa

Product Overview

Non-wetting aluminum castable is made by adding the composite ultra-fine powder to the castable, so as to reduce the porosity to less than 10% and prevent the adhesion and penetration of molten aluminum liquid.

Characters

In the aluminum smelting process, The castable is no-wetted in the molten aluminum, no slag, and no aluminum ash, which greatly reduces the reaction of aluminum liquid and refractory materials, and improve the quality of aluminum alloy.

Specification

Type high alumina
Material Non-stick aluminum refractory castable
Max working temp.(℃) 1550
Bulk density after drying at 110℃, g/cm3 2.80
Chemical analysis, % Al2O3≥ 80
SiO2≤ CaO 2%
Cold bending strength (Mpa) 110℃*24H 10
800℃*3H
1400℃*3H 12
Cold crushing strength
(Mpa)
110℃*24H 95
800℃*3H
1400℃*3H 90
Linear change after heating, % 800℃*3H
1400℃*3H -0.3
Water Addition As per supplier formula
Construction method Vibration
Application Lower furnace wall and bottom of melting aluminum furnace

Message

Please feel free to give your inquiry in the form below. We will reply you in 24 hours.

Related Products

Related Solutions

  • cement rotary kiln lining refractories

    Refractory lining material recommendation for cement rotary kiln

  • fire brick for lime kiln

    Refractories recommendation for vertical shaft lime kiln lining

  • tunnel kiln refractory brick

    Shuttle kiln and tunnel kiln lining Refractories Recommendation

Top Online Service [email protected]