Clay refractory bricks are the most widely used refract…
Raw material: chamotte clay
Straight size: 230*114*65mm (9”*4.5”*2.5”)
Max service temp：1300℃
Application: various industrial furnace lings
Capacity: 100 tons/day
Package: wooden pallet
Clay refractory bricks are the most widely used refractories made from chamotte clay minerals and calcined at a high temperature of 1300 to 1400 ° C.. It can be easily located out in the nature and contains suitable content ratio of silica, cyanite and alumina. Fire clay bricks have low porosity and are durable for various re-heating process.
Clay bricks are widely used in metallurgy, blast furnaces and hot blast furnaces, chemical industries waste incinerators, glass melting furnaces. It is the first selection of thermal equipment permanent lining material. Fire clay brick is mainly used in the low temperature parts of various industrial furnaces, due to the scale-up of a variety of industrial furnaces and severity of operating conditions, super dense clay bricks that made of more refined chamotte being calcinated at high temperature are applied more than before.
| Item | Chemical & Physical Properties | ||||||||
| N-1 | N-2a | N-2b | N-3a | N-3b | N-4 | N-5 | N-6 | ||
| Refractoriness ≥ | 1750 | 1730 | 1730 | 1710 | 1710 | 1690 | 1670 | 1580 | |
| Load softening temperature ≥ | 1400 | 1350 | 1320 | 1300 | |||||
| Rebirth line change rate | 1400℃×,2h | 0.1 | 0.1 | 0.2 | 0.2 | ||||
| -0.4 | -0.5 | -0.5 | -0.5 | ||||||
| % ≥ | 1350℃×,2h | 0.2 | 0.2 | 0.2 | 0.2 | ||||
| -0.5 | -0.5 | -0.5 | -0.5 | ||||||
| Apparent porosity % ≥ | 22 | 24 | 26 | 24 | 26 | 24 | 26 | 28 | |
| Crushing strength Kgf/cm2 ≥ | 30 | 25 | 20 | 20 | 15 | 20 | 15 | 15 | |
| Thermal shock stability | 300 | 250 | 200 | 200 | 150 | 2 | |||